Product Details
YLF-81W2
Meet the Standards： |
AWS A5.29 E81T1-W2C AWS A5.36M E551T1-C1A3-W2 |
ISO 17632-B T553T1-1CA NCC1 |
Element | C | Mn | Si |
Standard Value | ≤0.12 | 0.50-1.30 | 0.35-0.80 |
Typical Value | 0.04 | 0.60 | 0.35 |
S | P | Ni | Cu |
≤0.030 | ≤0.030 | 0.40-0.80 | 0.30-0.75 |
0.012 | 0.014 | 0.67 | 0.36 |
Weld Metal Mechanical Properties:
Mechanical Properties | Yield Strength (MPa) | Tensile Strength(MPa) | Elongation(%) | Impact ValueJ/°C |
Typical Value | 515 | 590 | 25 | 90/-30 |
Radiographic testing requirement for welds: Grade I
Shielding Gas: CO₂
Precautions:
1. For multi-pass welding, the interpass temperature shall be controlled between 135 °C and 165 °C.
2. The shielding gas flow rate shall be maintained at approximately 15–25 L/min.
3. Prior to welding, remove all impurities from the base metal surface, including rust, primer, oil, grease, carbon-arc gouging scale, and welding slag.
Description:
1.YLF-81W2 is a gas-shielded flux-cored wire designed for 550 MPa weathering steels.
2.The deposited metal contains Cu, Ni, and Cr, providing good atmospheric corrosion resistance and excellent crack resistance.
3.It offers excellent all-position weldability with low fume emission, a soft and stable arc, complete slag coverage, and very easy slag removal. Radiographic testing performance is excellent.
Applications:
Bridges, motorcycles, and automobiles.
Main Chemical Composition of the Welding Wire((%)
YLF-711
YLF-711Ni
YLF-81K2