Product Details
Meet the standards： |
GB/T5293 S55A5U/6UFB-SUN21 |
AWS A5.23 F8A8-ENi1K-Ni1 |
ISO 14174-S A FB 1 |
Flux Composition：
Particle Size | Flux testing% | ||||
Moisture Content | Impurity Content | S | P | ||
GB | 10-60 | ≤0.10 | ≤0.30 | ≤0.03 | ≤0.04 |
Typical Value | 10-40 | 0.012 | 0.015 | 0.055 | 0.032 |
Mechanical Properties of Deposited Metal:
Matching Welding wire | Tensile Strength | Yield Strength | Elongation | Impact Value | ||||
Mpa | Mpa | % | J/℃ | |||||
Typical Value | ENi1K/4mm | 595 | 550 | 28 | 138/-60 | |||
H08MnMo/4mm | 630 | 540 | 26 | 90/-50 | ||||
Precautions:
1. The flux shall be dried at 300–350 °C for 2 hours before use.
2.Prior to welding, impurities such as rust, primer, oil, grease, carbon-arc gouging scale, and welding slag shall be removed from the base metal surface.
3.The flux may be reused, however, at least 20% new flux shall be added each time to maintain the welding process performance and the mechanical properties of the weld metal.
Features and Applications：
1. SJ102NQ is a fluorine-basic, high-basicity agglomerated flux. It is a specially developed flux that minimizes alloy loss in the weld metal.
2.When paired with suitable welding wires, it is suitable for welding pressure vessels, shipbuilding, steel structures, bridges, wind towers, and similar applications.
SJ101
SJ101G
SJ105Q
SJ301